UHMW Polyethylene Film

Extremely high abrasion resistance, exceeding the abrasion resistance of steel. Coupled with broad chemical resistance and low coefficient of friction makes UHMW an extremely versatile engineering material for many severe service applications. Slippery like Teflon® but super abrasion & wear resistant. UHMW Polymers have a molecular weight average 10 times that of conventional high density polyethylene resins. Higher molecular weight gives UHMW Polymers its unique combination of characteristics Applications: Inner and outer surfaces for potable water, chemical, fuel and hydraulic hoses, bottom surfaces for skis and snow boards, linings for chutes to decrease friction and wear. Automotive weather stripping. (Also available with adhesive, UHMW Tape)

The highest abrasion resistance of any thermoplastic polymer
Outstanding impact strength even at very low temperatures
An excellent sliding material due to the low coefficient of friction
Self-lubricating (non-caking and sticking)
Sound dampening properties
Good chemical and stress cracking resistance
Easily machined
FDA and USDA approved

UHMW-PE THIN GAUGE (.003 to .020")

PRODUCT DESCRIPTION

Skived Ultra High Molecular Weight Polyethylene film (UHMW).

Technical Data - UHMW Film

PROPERTY	TEST METHOD	DATA
Tensile Strength (psi)	ASTM-D 882	6,000
Elongation (%)	ASTM-D 882	300
Dielectric Strength (Volts)	ASTM-D 149	3,000
Dielectric Constant (2H 10^6 Hz)	ASTM-D 150	2.3
Specific Gravity/Density (g/cc)		.93
Dissipation Factor	ASTM-D 150	.0004
Deformation (%)	2000 PSI, 6HR, 122F	6-8
Coefficient of Thermal Expansion (in/in/F)		11x10^4
Heat Distortion Temp. (F)	ISO R75 METHOD A	203
Thermal Conductivity (73 F)(BTUin)/(ft^2hrF)		.44
Water Absorption (%)		.01

UHMW Properties THICK GAUGES (.030" to .125")
MECHANICAL PROPERTIES

PROPERTY	ASTM TEST	UNITS METRIC (U.S)	.030"	.060"	.125"
Density	D792	gm/cc	0.93	0.93	0.93
Tensile Strength @ Yield	D638	MPa(psi)	23(3300)	20(2964)	22(3227)
Tensile Strength @ Break	D638	MPa(psi)	53(7740)	49(7056)	44(6373)
Elongation @ Break	D638	%	460	463	466
Youngs "E" Modulus	D638	MPa(psi x 105)	725(1.05)	731(1.06)	672(0.97)
Izod Impact Strength (23^oC)	D256(1)	J/m(ft-lb/in notch)
Izod Impact Strength (-40^oC)	D256(1)	J/m(ft-lb/in notch)
Hardness Shore "D"	D2240	-	65	65	65
Abrasion Resistance
Water Absorbtion	D570	%	Nil	Nil	Nil
Relative Solution Viscosity	D4020	dl/gm	2.3 - 3.5	2.3 - 3.5	2.3 - 3.5
COEFFICIENT OF FRICTION
Static			0.16	0.16	0.16
Dynamic			0.14	0.13	0.14

(1) Izod Impact Strength: Samples have two(15o +/- 1/2o) notches on opposite sides to a depth of 5mm.

COMPARISON OF DYNAMIC COEFFICIENT OF FRICTION ON POLISHED STEEL

PROPERTY	DRY	WATER	OIL
UHMW-PE	.10-.22	.05-.10	.05-.08
NYLON 6	.15-.40	.14-.19	.02-.11
NYLON 6/6	.15-.40	.14-.19	.02-.11
NYLON/MoS2	.12-.20	.10-.12	.08-.10
PTFE	.04-.25	.04-.08	.04-.05
Acetal COPOLYMER	.15-.35	.10-.20	.05-.10

THERMAL PROPERTIES

PROPERTY	ASTM TEST	UNITS METRIC (U.S)	.030"	.060"	.125"
Crystalline Melting Range	Polarizing	^oC(^oF)	136(276)	134(273)	134(273)
Crystallinity	D3417-96	%	48	47	50
COEFFICIENT OF LINEAR EXPANSION
20 - 100^oC	D696	TBD	TBD	TBD	TBD
-20 to -100^oC	D696	TBD	TBD	TBD	TBD

ELECTRICAL PROPERTIES

PROPERTY	ASTM TEST	UNITS METRIC (U.S)	.030"	.060"	.125"
Volume Resistivity	D357	Ohms/cm	5.9544x10^7	1.4516x10^7	>2.000x10^13
Dielectric Strength	D150	KV/cm (V/mil)	*	*	142
Dielectric Constant	D150		2.481	2.454	2.542
Surface Resistivity 1% Carbon Black	D257	Ohms	10^3	10^3	10^3
Static Decay 1% Carbon Black		Seconds	<.01	<.01	<.01
DISSIPATION FACTOR
At 50Hz	D150		0.0594	0.0213	0.0082
At 10KHz	D150		0.1085	0.0690	0.0022
At 5MHz	D150		0.1035	0.2340	0.0034

* No reading could be taken due to material thickness.

ADHESIVE PROPERTIES

Adhesion, 180i Peel	2 mil	(0.05 mm)	Polyester Support
	U.S. POUNDS FORCE PER INCH WIDTH	METRIC NEWTONS PER METER
Substrate: Stainless Steel (Applied One Minute)	175	1975
LOOP TACK
Substrate: Stainless Steel	288	3135
STATIC SHEAR
Temperature	Area	Load	Minutes to Failure
72iF(22iC)	1"(6.5cm2)	5.5 lbs(2.5kg)	>10,000
FEATURES	BENEFITS	STORAGE, SHELF LIFE & TEMP. INFO	SURFACE PREPARATION
Polypropylene Carrier	Stability in Processing	One year when stored at 70i F(21i C)	It is essential, as with all pressure-sensitive tapes, that the surface to which the tape is applied be clean, dry, and free of grease and oil.
Specially Formulated Adhesive	Combines high tack and adhesion with excellent shear	Minimum Application Temperature: 50i F(10i C) Maximum Continuous Operating Temperature: 120i F(49i C) Maximum Intermittent Operating Temperature: 175i F(79i C)

CS Hyde Company, Inc.
1351 N Milwaukee Avenue, Lake Villa, Illinois 60046
Phone: 800-461-4161 / 847-395-0325
Fax: 800-441-8063

Teflon® is a Registered Trademarks of E.I. du Pont de Nemours and Company used under license by CS Hyde Company.

Rulon®, Strip-N-Stick are registered trademarks of Saint GoBain Performance Plastics Corporation, Solef® is a registered trademarks of Solvay Solexis

C4-NGen® and KYNStick® are registered trade names of CS Hyde Company,

Ultem® is a registered trademarks of GE Plastics Ultrason®E is a registered trademarks of BASF Corporation, TPX® is a registered trademark of Mitsui Chemicals, Inc.

Halar® and Udel® are registered trademarks of Solvay Solexis, Inc, Mylar® is a registered trade name of DuPont Teijin Films.

PROPERTY

ASTM TEST

UNITS METRIC (U.S)

.030"

.060"

.125"

PROPERTY

DRY

WATER

OIL

PROPERTY

ASTM TEST

UNITS METRIC (U.S)

.030"

.060"

.125"

PROPERTY

ASTM TEST

UNITS METRIC (U.S)

.030"

.060"

.125"

* No reading could be taken due to material thickness.